精品国产综合久久_欧美日韩精品免费观看视一区二区_国产又爽又黄的激情精品视频_国产偷久久久精品专区

5CrNiMo|Φ6 軋材   低耐熱性模具鋼
5CrNiMo|Φ8 軋材   低耐熱性模具鋼
5CrNiMo|Φ10 軋材  低耐熱性模具鋼
5CrNiMo|Φ11 軋材  低耐熱性模具鋼
5CrNiMo|Φ12 軋材  低耐熱性模具鋼
5CrNiMo|Φ13 軋材  低耐熱性模具鋼
5CrNiMo|Φ14 軋材  低耐熱性模具鋼
5CrNiMo|Φ15 軋材  低耐熱性模具鋼
5CrNiMo|Φ16 軋材  低耐熱性模具鋼
5CrNiMo|Φ17 軋材  低耐熱性模具鋼
5CrNiMo|Φ18 軋材  低耐熱性模具鋼
5CrNiMo|Φ19 軋材  低耐熱性模具鋼
5CrNiMo|Φ20 軋材  低耐熱性模具鋼
5CrNiMo|Φ21 軋材  低耐熱性模具鋼
5CrNiMo|Φ22 軋材  低耐熱性模具鋼
5CrNiMo|Φ23 軋材  低耐熱性模具鋼
5CrNiMo|Φ24 軋材  低耐熱性模具鋼
5CrNiMo|Φ25 軋材  低耐熱性模具鋼
5CrNiMo|Φ26 軋材  低耐熱性模具鋼
5CrNiMo|Φ28 軋材  低耐熱性模具鋼
5CrNiMo|Φ29 軋材  低耐熱性模具鋼
5CrNiMo|Φ30 軋材  低耐熱性模具鋼
5CrNiMo|Φ32 軋材  低耐熱性模具鋼
5CrNiMo|Φ35 軋材  低耐熱性模具鋼
5CrNiMo|Φ38 軋材  低耐熱性模具鋼
5CrNiMo|Φ40 軋材  低耐熱性模具鋼
5CrNiMo|Φ42 軋材  低耐熱性模具鋼
5CrNiMo|Φ45 軋材  低耐熱性模具鋼
5CrNiMo|Φ48 軋材  低耐熱性模具鋼
5CrNiMo|Φ50 軋材  低耐熱性模具鋼
5CrNiMo|Φ130 鍛材  低耐熱性模具鋼
5CrNiMo|Φ140 鍛材  低耐熱性模具鋼
5CrNiMo|Φ145 鍛材  低耐熱性模具鋼
5CrNiMo|Φ150 鍛材  低耐熱性模具鋼
5CrNiMo|Φ155 鍛材  低耐熱性模具鋼
5CrNiMo|Φ160 鍛材  低耐熱性模具鋼
5CrNiMo|Φ165 鍛材  低耐熱性模具鋼
5CrNiMo|Φ170 鍛材  低耐熱性模具鋼
5CrNiMo|Φ175 鍛材  低耐熱性模具鋼
5CrNiMo|Φ180 鍛材  低耐熱性模具鋼
5CrNiMo|Φ185 鍛材  低耐熱性模具鋼
5CrNiMo|Φ190 鍛材  低耐熱性模具鋼
5CrNiMo|Φ195 鍛材  低耐熱性模具鋼
5CrNiMo|Φ200 鍛材  低耐熱性模具鋼
---------------------------------
材料名稱：合金工具鋼

牌號：5CrNiMo

標準：GB/T 1299-1985

●特性及適用范圍：

5CrNiMo鋼具有良好的韌性、強度和高耐磨性。它在室溫和500～600℃時的力學性能幾乎相同。在加熱到500℃時，仍能保持住HB300左右的硬度。由于鋼中含有鉬，因而對回火脆性并不敏感。從600℃緩慢冷卻下來以后，沖擊韌性僅稍有降低。

5CrNiMo鋼具有良好的淬透性。300mm×400mm×300mm的大塊鋼料，自820℃油淬和560℃回火后，斷面各部分的硬度幾乎一致。

該種鋼用來制造各種大、中型鍛模。易形成白點，需要嚴格控制冶煉工藝及鍛軋后的冷卻制度。

●化學成份：

碳 C ：0.50～0.60

硅 Si：≤0.40

錳 Mn：0.50～0.80

硫 S ：≤0.030

磷 P ：≤0.030

鉻 Cr：0.50～0.80

鎳 Ni：1.40～1.80

銅 Cu：允許殘余含量≤0.30

釩 V ：允許殘余含量＜0.2

鉬 Mo：0.15～0.30

●力學性能：

硬度 ：退火,241～197HB,壓痕直徑3.9～4.3mm

●熱處理規范及金相組織：

熱處理規范：淬火,830～860℃油冷。

●交貨狀態：鋼材以退火狀態交貨。